Activated carbon adsorbents with micro-mesoporous structure derived from waste biomass by stepwise activation for toluene removal from air
发布时间：2024-11-30
点击次数：
- 影响因子：
- 7.968
- DOI码：
- 10.1016/j.jece.2021.105387
- 所属单位：
- 重庆工商大学
- 教研室：
- 化学工程系
- 发表刊物：
- Journal of Environmental Chemical Engineering
- 项目来源：
- 重庆市教育委员会，重庆市科技局
- 关键字：
- Waste biomass；Activated carbon adsorbent；Micro-mesoporous structure；Toluene；Adsorption removal
- 摘要：
- The waste biomass was used as raw materials to prepare activated carbon adsorbents with micro-mesoporous structure. And the prepared activated carbon adsorbents were used to adsorption remove toluene from air, which can achieve the goal of “treat waste with waste”. In this paper, biomass activated carbon adsorbents with micro‒mesoporous structure were prepared by two-stage process of “low temperature carbonization‒high temperature activation” using waste biomass as raw materials and H3PO4 as activator. The obtained results show that the activation temperature can significantly affect the structural characteristics, graphitization degree and surface chemical properties of the prepared adsorbents, and the toluene adsorption and regeneration performances of the adsorbent are significantly affected by its physicochemical properties. High thermal desorption temperature (100 ◦C) can destroy the strong interaction between the oxygen atoms of the oxygen-containing functional groups on the surface of the adsorbent and the p-electrons of toluene aromatic ring, thus realizing the desorption of corresponding adsorbed toluene molecules. The low heat treatment temperature of 60 ◦C can destroy the strong adsorption from narrow micropores for toluene and π‒π conjugation effect between the adsorbent and toluene molecules, which can realize the corresponding adsorbed toluene molecules to be desorbed. When the activation temperature is 650 ◦C, the activated carbon adsorbent with surface area of 1006.2 m2/g, micro-mesoporous structure and mesoporous proportion of 65.5% can be prepared. The adsorption capacity of toluene can reach 417.0 mg/g, and the toluene thermal desorption regeneration can be realized at 60 ◦C. The results indicate that it is a promising adsorbent material for toluene removal from air.
- 第一作者：
- Guizhi Zhang,Bingman Lei
- 合写作者：
- Shengming Chen,Hongmei Xie
- 论文类型：
- 源刊论文
- 通讯作者：
- Guilin Zhou
- 学科门类：
- 工学
- 文献类型：
- Journal Article
- 卷号：
- 9
- 期号：
- 4
- 页面范围：
- 105387
- 是否译文：
- 否
- 发表时间：
- 2021-08-02
- 收录刊物：
- SCI